Technical Datasheet POM 100P

Product Description:

Delrin® 100P is a high viscosity acetal homopolymer for use in easy to fill molds. Delrin® 100P provides maximum toughness in the product line without modification. Delrin ® 100P has improved processing thermal stability.

Applications:

Injection molding of industrial parts.

Typical data:

PROPERTY TEST METHOD UNIT TYPICAL VALUE
Resin Identification ISO 1043   POM
Part Marking Code ISO 11469   >POM<
Yield Stress ISO 527 MPa 70
Yield Strain ISO 527 % 25
Strain at Break 50mm/min ISO 527 % 65
Nominal Strain at Break ISO 527 % 45
Tensile Modulus ISO 527 MPa 2900

Tensile Creep Modulus

1h

1000h

ISO 899 MPa

 

2700

1500

Flexural Modulus ISO 178 MPa 2600
Flexural Stress @ 3.5% Strain ISO 178 MPa 74

Notched Charpy Impact Strength

-30°C

23°C

ISO 179/1eA kJ/m2

 

11

14

Unnotched Charpy Impact Strength

-30°C

23°C

ISO 179/1eU kJ/m2

 

350

NB

Deflection Temperature

0.45Mpa

1.80Mpa

ISO 75-1/-2 °C

 

160

93

Melting Temperature 10°C/min ISO 11357-1/-3 °C 178

CLTE, Parallel

-40 - 23°C

23 - 55°C

55 - 100°C

ISO 11359-1/-2 E-4/C

 

1.0

1.1

1.5

CLTE, Normal

-40 - 23°C

23 - 55°C

55 - 100°C

ISO 11359-1/-2 E-4/C

 

1.0

1.1

1.5

Vicat Softening Temperature 50N ISO 306 °C 157
Melt Mass-Flow Rate 190°C, 2.16kg ISO 1133 g/10 min 2.5
Density ISO 1183 kg/m3 1420

Hardness, Rockwell

Scale M

Scale R

ISO 2039/2  

 

92

120

Water Absorption

Equilibrium 50%RH

Saturation, immersed

ISO 62, Similar to %

 

0.3

1.4

Molding Shrinkage

Normal, 2.0mm

Parallel, 2.0mm

ISO 294-4 %

 

2.0

2.2

* Typical values not to be construed as specifications.