پلی کربنات 110 PC


پلی كربنات 110 یك پلی كربنات با جریان پذیری متوسط می‌باشد كه خواص مكانیكی و چقرمگی عالی دارد. كاربرد آن در صنایع خودرو و لوازم خانگی و قطعات صنعتی و بسته بندی مواد غذایی می‌باشد.


فایل PDF

Technical Datasheet PC-110

Product Description:

PC-110 is a medium viscosity Polycarbonate resin polymerized using the double hydroxy compounds of BPA (bisphenol-A) and the diphenylcarbonates of carbonate compounds with the transesterification (melting) method. Absolutely no phosgene and chlorinated solvents such as dichloromethane were used during the manufacturing process. PC-110 is FDA and UL certified. PC-110 has excellent transparency, high heat resistance, ultra high impact resistance, dimensional stability, etc., making it suitable for a wide range of applications.

Applications:

Vehicle indicator light casings, mouse, chocolate container boxes, high heel shoes.

Typical data:

PROPERTY TEST METHOD TEST CONDITION UNIT TYPICAL VALUE
Melt Flow Index ASTM D1238 300 ℃, 1.2 Kg g/10 min 10.0
Mass Density ASTM D792 23 ℃ - 1.2
Hardness ASTM D785 - M Scale 77
Tensile Strength (Yield) ASTM D638 6 mm/min Kg/cm2 630
Tensile Strength (Yield) ASTM D638 6 mm/min lb/in2 8935
Tensile Elongation ASTM D638 6 mm/min % 110
Flexural Strength ASTM D790 1.3 mm/min Kg/cm2 920
Flexural Strength ASTM D790 1.3 mm/min lb/in2 13030
Flexural Modulus ASTM D790 1.3 mm/min 104 Kg/cm2 2.4
Flexural Modulus ASTM D790 1.3 mm/min 105 lb/in2 3.4
Izod Impact Strength ASTM D256 3.2 mm, 23℃ Kg-cm/cm 87
Izod Impact Strength ASTM D256 3.2 mm, 23℃ ft-lb/in 15.9
Vicat Softening Temp. ASTM D1525 1 Kg,50 ℃/hr °C 150
Heat Distortion Temp. ASTM D648 132℃×8 hours Loading 4.6 kg/cm2 °C 146
UL Flammability UL 94 - - 1.5mm v-2

* Typical values not to be construed as specifications.cm